Nickel wire mesh

Nickel Nickel Grade Nickel 200 Nickel 201 Nickel 205 Nickel 233

Physical and Mechanical Properties Tensile Strength ksi 65 MPa 449 Yield Strength ksi 20 MPa 138 Melting point 1728K/2651ºF/1455 ºC Hardness HB 335(25 ºC)

Characteristics: 1. Good resistance to corrosion in acids and alkalis and is most useful under reducing conditions. 2. Outstanding resistance to caustic alkalis up to and including the molten state. 3. Virtually immune to inter granular attack above 315 ºC, chlorates must be kept to a minimum. 4.

In acid, alkaline and neutral salt solutions the material shows good resistance, but in oxidising salt solutions severe attack will occur. 5. Resistant to all dry gases at room temperature and in dry chlorine and hydrogen chloride may be used in temperatures up to 550 ºC. 6.

Resistance to mineral acids varies according to temperature and concentration and whether the solution is aerated or not. Corrosion resistance is better in de-aerated acid.

Applications: 1. Fittings, fasteners exposed to high temperatures in steel mills and power plants. 2. Stainless steel pipe fittings, flanges, pump fittings. 3. Fasteners in exhaust manifolds and boilers. 4. Steam generators. 5. Assembly of dissimilar metals.

Specification Wire ASTM B160 Diameter:0.05mm-10.0mm, 0.002 Inch to 0.3937 Inch Wire Mesh GB/T 5330.1 GB/T 17492 JB/T 9155 0.5-250 mesh/Inch Thickness: Min0.05mm Sheet SJ 20151-1992 Thickness: 0.05mm and above