Malaysia Alpha 2000 & ALPHA 2000-HD

Specifications: CHEMTOOL ALPHA 2000 & ALPHA 2000-HD is made of totally new and exclusive proprietary CSC thickener blended with high viscosity premium base oil. ADVANTAGES: (1) ALPHA 2000 & 2000-HD state-of-the-art CSC thickener (up to 30%) inherent extreme pressure & anti wear properties, apart from acting as an agent to carry the base oil.

Other premium greases that are usually blended with very little quantity of anti wear additives tends to fail when their EP and AW additives have been exhausted. (2) Both demonstrated very little change in the consistency and will not soften due to repetitive shearing and loading.

(3) Shell Roll test was then modified from six hours at room temperature to 100 hours at 65.5C to increase the severity and again, no softening was observed on ALPHA 2000 & 2000-HD. (4) Both have high viscosity of its mineral base oil ( for ALPHA 2000 & for ALPHA 2000-HD). This also means ALPHA 2000 has tremendous load carrying abilities.

(5) ALPHA 2000 and 2000-HD surpassed Lubrication Life Test. (6) In Wheel Bearing Test ALPHA 2000 & 2000-HD shows no sign of leakage or hardening that may lead to bearing failure. (7) ALPHA 2000 & 2000-HD has excellent resistance to oxidation.

APPLICATIONS: (1) Specific applications include lubricating medium-to-large anti-friction bearings that operates at high load, high temperature and exposure to cooling water. (2) Steel mills & cement plant: Spherical roller bearings in cold rolling mill; tapered roller bearings in hot rolling mills; double spherical bearings in caster and withdrawal.

(3) Marine grease: quay-line, shore side gantry cranes turret bearings.

(4) Agricultural/ construction (fifth wheels, king pins and bearings grease) (6) Industrial (painting conveyor roller bearings grease) SPECIFICATIONS: NLGI Grade: 2 Colour: Tan Texture: Smooth Work Penetration D-217 (60 strokes): 270 Work Penetration D-217 (100,000 strokes):+2 Dropping Point D-2265: 315C Oxidation Stability D-942 (psi drop/ 100 hours): 0 psi Oxidation Stability D-942 (psi drop/ 500 hours): 2 psi Oxidation Stability D-942 (psi drop/ 1000 hours): 9 psi Corrosion Prevention D-1743: Pass Water Washout D-264 (79.4C): 2.75% Timken Load D-2509: 65lbs (29.5kg) 4 Ball EP Weld Point D-2596: 500kg Load Wear Index D-2596: 65kg 4 Ball Wear Scar Diameter D-2266 (40kg, 1200rpm, 75C, 1hr): 0.39mm Roll Stability Test D-1831: +19 Oil Separation D-1742, 24 hours 25C: 0.17% Wheel Bearing Leakage D-1263 (Modified to 79C): 0.4 Base Oil Viscosity D-445: ALPHA 2000-HD: & ALPHA 2000: & Viscosity Index: >130 Pour Point: -15C Working temperature: 177C AVAILABILITY: ALPHA 2000 & 2000-HD is available in 400 grams cartridges (one carton consists of 10 cartridges), 18kg pails and 181kg drums.

Also available in version of ALPHA 2000-HD with 3% Molybdenum Disulfide for dry film lubrication)