Cupolas

Qingli produces cupolas of various types like Side-lay type hot-blast external-combustion cupolas, Steel slag recovery cupolas, Water-cool cupola, Double-shift water-cool thin-lining cupola, hot air cupola, cold air cupola and so on.

Side-lay type

We develop RC-W-N hot-blast external-combustion cupola by combining the introduced advanced technology with the actual situation in China, which can well raise the tapping temperature, get a stable chemical composition and improve the product quality. At the same time it can also decrease the CO emission, low down the coke consumption and the burning losses and eventually decrease the production cost.
Basic parameters

Tapping temperature>1500

Hot air entering temperature 400℃600℃

Coke consumption ratio1:8~1:10

Stable chemical composition, low FeO content, long campaign of 30 days above, productivity of 5T/h~50T/h, rate of certified product raised by 20%-30%.

is a kind of reductive cupola system which was developed from hot-blast external-combustion cupola system. This type of cupola can use s as melting materials to produce steel pig or foundry pig of various grades.
system consists of furnace, combustion room, heat exchanger, charging system and de-dusting system, which can be developed into various types like single shift cupola, double shift cupola, or long campaign cupola at customer’s requests. And can work 24hours×30 days above, while the tapping hole repair may cost 4~5hours every 510days. If any errors during melting process, it can temporarily take a and bank up for error correction. After error correction, it can restore to normal melting.
The melting materials contain a 20%~30% , which can mostly(≥94 in general) be restored to iron product under high-temperature condition. The high-temperature condition favors to resiliconize(>1% generally ) and recarburize(varied in accordance with furnace specifications), too. Values above may vary according to the actual material grade/ chemical composition.