SBR|tpe|SEBS|YH-501|Hot melt adhesive - SEBS YH-501 Specificaton & Trade Terms
| Model | SEBS YH-501 |
|---|
| Place Of Origin | Baling Petrochemical,Yueyang,Hunan,China |
|---|
| Price Term | EX-Work |
|---|
| Payment Term | T/T |
|---|
Typical Properties：
Structure: Radial
Styrene content 30%（Weight）
Tensile strength: 20Mpa
Stress at 300%:4.0Mpa
Elongation:500%
Hardness shore(A): 75
Toluene solutioh viscosity(10%,25℃,Mpa):500mpa.s
Appearance: white powder
2.Main application
YH-501 as a kind of low molecular weight linear SEBS, owing to it's good liquidity and low viscosity solution, can be used in the production of hot melt (psa) rubber and plastic modification, etc.
Detailed introduction to Sinopec SEBS YH-501:
YH-501 for low molecular weight linear SEBS, with good fluidity and melting characteristics of low viscosity can be used to produce hot-melt (pressure sensitive) Rubber and Plastic Modification and so on.
YH-501 produced using hot-melt pressure-sensitive adhesive tack, peel strength is moderate, good cohesion, and can be used to produce packaging to protect film; in YH-501 by adding an appropriate amount of SIS, can effectively increase their hot-melt pressure-sensitive tack adhesive strength and peel strength, can be prepared by high-performance pressure-sensitive adhesive. YH-501 has a flow of hot melt adhesives produced good performance, good creep resistance, anti-aging characteristics of high cohesive strength can be used to produce high-grade carpet, anti-slip mats on the back of glue; can also be used for wood production , paper, fabric, leather, metal, plastic, etc. The hot melt adhesive.
YH-501 can be used for PP, PS, LDPE, HDPE, PPO, etc. toughening modification, can significantly improve the low-temperature brittleness, for the modification of PP, it can keep the material transparency. The amount of modified plastics is usually 5-20%.